The workability, compressive strength, flexural strength, and electrical conductivity of smart high-performance concretes containing graphite and steel fiber

Le Huy Viet , Duong Tuan Trung

Keywords:

Flexural strength
Graphite
Smart high-performance concrete
Steel fiber
Workability
Electrical resistivity
Compressive strength

Abstract

Smart high-performance concretes (SHPCs) containing highly electrically conductive functional fillers (FFs) were a new type of material to apply for structural health monitoring systems or smart city infrastructures. This study investigated the mechanical properties, such as the compressive strength, flexural strength, and the electrical resistivity of SHPCs incorporating graphite powder (0 to 5% of cement by weight) and steel fibers as FFs (0 to 2 vol%). The electrical resistivity of each specimen was measured using a direct current (DC) with the two-probe method to evaluate the conductivity of SHPCs. The results indicated that the addition of graphite decreased the workability, compressive, and flexural strengths but notably increased the electrical conductivity of SHPCs. The SHPCs containing 5% graphite and 1 vol% steel fibers produced the highest compressive strength (72.8 MPa) and flexural strength (14.7 MPa) in comparison with SHPCs containing 5% graphite and other fiber contents. As the fiber volume content increased from 0 to 2 vol%, the volume weight of SHPCs varied from 2216 to 2363 kg/m3. The flexural strength per compressive strength of SHPCs was varied from 18.7 to 20.1%. In addition, the electrical conductivity of the SHPCs showed a notable increase with higher contents of graphite and steel fibers, forming effective conductive networks within the concrete matrix. The findings suggest that the integration of graphite and steel fibers can effectively improve the multifunctional performance of SHPCs, making them suitable for structural health monitoring applications in advanced civil infrastructure.

User Navigation

PDF

How to Cite

Le, H. V., & Duong, T. T. (2025). The workability, compressive strength, flexural strength, and electrical conductivity of smart high-performance concretes containing graphite and steel fiber. JOURNAL OF MATERIALS & CONSTRUCTION, 15(01), Page 195 – Page 202. https://doi.org/10.54772/jomc.v15i01.1020

References

  1. B. Han, X. Yu, and J. Ou, Self-sensing concrete in smart structures. Kidlington: Butterworth Heinemann, Elsevier, 2014. doi: 10.1016/C2013-0-14456-X.
  2. S. Ding et al., “Self-Sensing Cementitious Composites with Hierarchical Carbon Fiber-Carbon Nanotube Composite Fillers for Crack Development Monitoring of a Maglev Girder,” Small, vol. 19, no. 9, Mar. 2023, doi: 10.1002/smll.202206258.
  3. B. Han, X. Yu, and E. Kwon, “A self-sensing carbon nanotube/cement composite for traffic monitoring,” Nanotechnology, vol. 20, no. 445501, pp. 1–5, 2009, doi: 10.1088/0957-4484/20/44/445501.
  4. J. Song, D. L. Nguyen, C. Manathamsombat, and D. J. Kim, “Effect of fiber volume content on electromechanical behavior of strain-hardening steel-fiber-reinforced cementitious composites,” J. Compos. Mater., vol. 49, no. 29, pp. 3621–3634, 2015, doi: 10.1177/0021998314568169.
  5. H. V. Le, D. H. Lee, and D. J. Kim, “Effects of steel slag aggregate size and content on piezoresistive responses of smart ultra-high-performance fiber-reinforced concretes,” Sensors Actuators, A Phys., vol. 305, p. 111925, 2020, doi: 10.1016/j.sna.2020.111925.
  6. S. Y. Lee, H. V. Le, and D. J. Kim, “Self-stress sensing smart concrete containing fine steel slag aggregates and steel fibers under high compressive stress,” Constr. Build. Mater., vol. 220, pp. 149–160, 2019, doi: 10.1016/j.conbuildmat.2019.05.197.
  7. L. H. Viet, L. Dao Phuc, N. T. Thuong, N. T. Thanh, D. L. Nguyen, and D. J. Kim, “Improvement of the stress sensing ability of ultra-high-performance concrete using short steel fibers and steel slag aggregates under high compression,” Sensors Actuators A. Phys., vol. 362, no. July, p. 114616, 2023, doi: 10.1016/j.sna.2023.114616.
  8. H. V. Le and D. J. Kim, “Detecting crack and damage location in self-sensing fiber reinforced cementitious composites,” Constr. Build. Mater., vol. 240, p. 117973, 2020, doi: 10.1016/j.conbuildmat.2019.117973.
  9. N. K. Lee, K. T. Koh, M. O. Kim, and G. S. Ryu, “Uncovering the role of micro silica in hydration of ultra-high performance concrete (UHPC),” Cem. Concr. Res., vol. 104, no. November 2017, pp. 68–79, 2018, doi: 10.1016/j.cemconres.2017.11.002.
  10. A. Dinesh, D. Suji, and M. Pichumani, “Self-sensing cementitious composite sensor with integrated steel fiber and carbonaceous powder for real-time application in large-scale infrastructures,” Sensors Actuators A Phys., vol. 353, no. February, p. 114209, 2023, doi: 10.1016/j.sna.2023.114209.
  11. D. Y. Yoo, I. You, and S. J. Lee, “Electrical and piezoresistive sensing capacities of cement paste with multi-walled carbon nanotubes,” Arch. Civ. Mech. Eng., vol. 18, no. 2, pp. 371–384, 2018, doi: 10.1016/j.acme.2017.09.007.
  12. H. V. Le et al., “Self-sensing characteristics of smart high-performance cementitious composites containing multiwall carbon nanotubes, steel fibers, and steel slag aggregates under compression,” Sensors Actuators A Phys., vol. 365, Jan. 2024, doi: 10.1016/j.sna.2023.114920.
  13. M. Cimesa and M. A. Moustafa, “Experimental characterization and analytical assessment of compressive behavior of carbon nanofibers enhanced UHPC,” Case Stud. Constr. Mater., vol. 17, no. July, p. e01487, 2022, doi: 10.1016/j.cscm.2022.e01487.
  14. L. H. Viet et al., “Nghiên cứu chế tạo bê tông hạt mịn cường độ chịu nén trên 100 MPa sử dụng hạt xỉ thép thay thế cát,” Tạp chí Vật liệu và xây dựng, vol. 6, pp. 45–50, 2023.
  15. H. V. Le, A. D. Do, V. M. Nguyen, T. K. Nguyen, and D. L. Nguyen, “Compressive and electrical resistivity properties of UHPC containing different steel fibers (Đặc trưng nén và điện trở suất của bê tông cường độ siêu cao sử dụng các loại sợi thép khác nhau),” Xây dựng, pp. 110–114, 2023.
  16. H. V. Le, D. Moon, and D. J. Kim, “Effects of ageing and storage conditions on the interfacial bond strength of steel fibers in mortars,” Constr. Build. Mater., vol. 170, pp. 129–141, 2018, doi: 10.1016/j.conbuildmat.2018.03.064.
  17. M. Zhao, X. Zhang, and Y. Zhang, “Effect of free water on the flowability of cement paste with chemical or mineral admixtures,” Constr. Build. Mater., vol. 111, pp. 571–579, 2016, doi: 10.1016/j.conbuildmat.2016.02.057.
  18. Tiêu chuẩn Việt Nam TCVN 3118:2022. 2022.
  19. D. L. Nguyen, J. Song, C. Manathamsombat, and D. J. Kim, “Comparative electromechanical damage-sensing behaviors of six strain-hardening steel fiber-reinforced cementitious composites under direct tension,” Compos. Part B Eng., vol. 69, pp. 159–168, 2014, doi: 10.1016/j.compositesb.2014.09.037.
  20. I. You, S. J. Lee, G. Zi, and D. Lim, “Influence of carbon fiber incorporation on electrical conductivity of cement composites,” Appl. Sci., vol. 10, no. 24, pp. 1–13, 2020, doi: 10.3390/app10248993.
  21. H. V. Le and D. J. Kim, “Effect of matrix cracking on electrical resistivity of high performance fiber reinforced cementitious composites in tension,” Constr. Build. Mater., vol. 156, pp. 750–760, 2017, doi: 10.1016/j.conbuildmat.2017.09.046.